Dongguan Ganghang Copper & Aluminum Co., Ltd.
0769-81666291
18038323201
合金牌号 |
Cu |
Pb |
Sn |
Zn |
P |
Cu+Sn+P |
||
C5111 |
3.5~4.5 |
0.03~0.35 |
99.5min |
|||||
C5102 |
4.5~5.5 |
0.03~0.35 |
99.5min |
|||||
C5191 |
5.5~7.0 |
0.03~0.35 |
99.5min |
|||||
C5212 |
7.0~9.0 |
0.03~0.35 |
99.5min |
|||||
C5341 |
0.8~1.5 |
3.5~3.8 |
0.03~0.35 |
99.5min |
||||
C5441 |
3.5~4.5 |
3.4~4.5 |
1.5~4.5 |
0.01~0.5 |
99.5min |
|||
Cu |
Sn |
Al |
Zn |
Ni |
Fe |
Pb |
P |
|
QSn6.5-0.1 |
余量 |
6.0~7.0 |
0.002 |
0.3 |
0.2 |
0.05 |
0.02 |
0.10~0.25 |
QSn4-3 |
余量 |
3.5~4.5 |
0.002 |
2.7~3.3 |
0.2 |
0.05 |
0.02 |
0.03 |
机械及物理性能 |
||||||||
Mechanicai properities |
||||||||
状态 |
拉伸试验 |
硬度试验 |
弯曲试验 |
|||||
厚度 |
拉伸强度 σb(MPa) |
伸长率 δ10(%) |
厚度 mm |
维氏硬度 HV |
厚度 mm |
弯曲角度 |
弯曲半径 |
|
O |
0.15-1.2 |
≥315 |
≥42 |
— |
— |
≤1.6 |
180°或w |
厚度×0.5 |
1/4H |
390-510 |
≥35 |
≥0.15 |
100-160 |
≤1.6 |
180°或w |
厚度×1 |
|
1/2H |
490-610 |
≥20 |
≥0.15 |
150-205 |
≤1.6 |
180°或w |
厚度×1.5 |
|
H |
590-685 |
≥8 |
≥0.15 |
180-230 |
≤1.6 |
180°或w |
厚度×2 |
|
EH |
≥635 |
≥5 |
≥0.15 |
≥200 |
— |
— |
— |
|
合金主要制作弹性元件特别是电导性好的弹簧接触片,仪器仪表中的耐磨零件和抗磁元件等 |
||||||||
合金主要用于造纸、化工和食品等工业制造金属网,也用于制造耐磨和弹簧零件 |
||||||||
合金用于在中等的载荷和滑动速度下承受摩擦的零件,如轴承、轴套、涡轮等,亦可制造弹性元件和其他机械电气零件 |
||||||||
合金用于生产压力表中的各种管材,作敏感元件,有压力表青铜之称 |